Holding magnet with facilitated separation 230x50x30 / N

Previous
Holding magnet with facilitated separation 250x100x30 / N
Holding magnet with facilitated separation 250x100x30 / N
Next
Holding magnet with facilitated separation 160x100x30 / N
Holding magnet with facilitated separation 160x100x30 / N
Holding magnet with facilitated separation 230x50x30 / NHolding magnet with facilitated separation 230x50x30 / N€112.50

Your Query is sent.

  •     *Required Fields

Loading

Of Price Net Price Gross
1 pcs. €112.50 €138.38
Quantity
Available Quantity: 3 pcs.

Uchwyt-magnetyczny-z-ulatwionym-odrywaniem-230x50x30--N

Performance parameters
Manufacturer
Enes
Length
230 [mm]
Width
50 [mm]
Height
30 [mm]
handle length
215 [mm]
threads quantity
3 [szt.]
thread type
wewnętrzny, M8
Material
Neodymium
maximal hoisting capacity
600 [kg]
recommended maximum thickness of the metal sheet
10 [mm]
Maximum working temperature
80 °[C]
Coating
Zinc (Zn)
with easier detachment
yes
handling mode
ręczny
With handle
yes
Weight
2.84 [kg]

The maximum pull force: ~600 [kg]

Three threaded holes M8.
Length of handle: ~215 [mm].
Total widht with handle: ~87 [mm]
.

Holding magnet with facilitated separation is used for secure of molds on vibro-tables during production of concrete elements.

In the holding magnet sintered neodymium magnets (NdFeB) were used. The maximum working temperature for holding magnets involving neodymium magnets is 80o[C].

The pull force given refers to hoisting capacity measured in optimal conditions, by using as a backing plate a sheet made of low-carbon steel, 10 [mm] thick, of smooth surface and with the force acting perpendicularly, in room temperature.

Notice: the pull force given should be treated as only a comparative value. An actual pull force depends on the following factors:

  • air gap (a distance) between holding magnet and an attracted element
  • material, of which an attracted element is made (the higher carbon proportion in steel, the smaller pull force)
  • surface of an attracted element (the smoother the surface, bigger the pull force)
  • direction of acting of detaching force (the biggest pull force is obtained with perpendicular acting of detaching force)
  • thickness of an attracted element (the element cannot be too thin, because in such case part of magnetic flux is not used for closing of a magnetic circuit)
  • working temperature.

We generally recommend individual checking of the holding magnet in any specific working conditions.

Weight of the holding magnet: ~2,8 [kg]

0

0

The maximum pull force: ~600 [kg]

Three threaded holes M8.
Length of handle: ~215 [mm].
Total widht with handle: ~87 [mm]
.

Holding magnet with facilitated separation is used for secure of molds on vibro-tables during production of concrete elements.

In the holding magnet sintered neodymium magnets (NdFeB) were used. The maximum working temperature for holding magnets involving neodymium magnets is 80o[C].

The pull force given refers to hoisting capacity measured in optimal conditions, by using as a backing plate a sheet made of low-carbon steel, 10 [mm] thick, of smooth surface and with the force acting perpendicularly, in room temperature.

Notice: the pull force given should be treated as only a comparative value. An actual pull force depends on the following factors:

  • air gap (a distance) between holding magnet and an attracted element
  • material, of which an attracted element is made (the higher carbon proportion in steel, the smaller pull force)
  • surface of an attracted element (the smoother the surface, bigger the pull force)
  • direction of acting of detaching force (the biggest pull force is obtained with perpendicular acting of detaching force)
  • thickness of an attracted element (the element cannot be too thin, because in such case part of magnetic flux is not used for closing of a magnetic circuit)
  • working temperature.

We generally recommend individual checking of the holding magnet in any specific working conditions.

Weight of the holding magnet: ~2,8 [kg]