D14 x d8/4 x 3 / N35 - NdFeB (neodymium) magnet

Previous
D14 x d3 x 7 / N35H - NdFeB (neodymium) magnet
D14 x d3 x 7 / N35H - NdFeB (neodymium) magnet
Next
D14,5 x d10,5 x 5 / N38 - NdFeB (neodymium) magnet
D14,5 x d10,5 x 5 / N38 - NdFeB (neodymium) magnet
D14 x d8/4 x 3 / N35 - NdFeB (neodymium) magnetD14 x d8/4 x 3 / N35 - NdFeB (neodymium) magnet€0.25

Your Query is sent.

  •     *Required Fields

Loading

Of Price Net Price Gross
1 pcs. €0.25 €0.31
700 pcs. €0.23 €0.28
1700 pcs. €0.22 €0.27
Quantity
Available Quantity: 4099 pcs.

d14-x-d84-x-3-n35-ndfeb-neodymium-magnet

Performance parameters
External diameter
14 [mm] +0,1/-0,1
aperture diameter for head of a screw
8 [mm] +0,1/-0,1
Internal diameter
4 [mm] +0,1/-0,1
Height
3 [mm] +0,1/-0,1
magnetizing direction along dimension
3 [mm]

Direction of magnetization along the height means that one circular surface of a magnet makes the N-pole, while the other – opposite – circular surface refers to the S-pole.
Material
Neodymium
Grade
N35
maximal hoisting capacity
2,5 [kg]

The pull force was measured by using metal sheet 10 [mm] thick, acting with perpendicular detaching force. The air gap comprised between the metal sheet and a magnet causes reduction in the pull force.
Magnetic field in geometrical center of the magnetic pole surface
0,278 [T]
Maximum working temperature
80 °[C]

For flat magnets and magnets mounted in the open magnetic circuit working temperature may be insignificantly lower. For high magnets and magnets mounted in the closed magnetic circuit working temperature equals max. working temperature for a given material. Curie’s temperature is ~ 310°[C]. Temperature coefficient of remanence TK(Br: approx. ~0,12 %/°[C]. Temperature coefficient of coercivity TK(HcJ): approx. -0,6 %/°[C].
Coating
Nickel (NiCuNi)
Magnetic moment
3560 [nWb]x[m]
Weight
2,9 [g]

All the numbers quoted were obtained as a result of tests with one specific item in a room temperature and are intended to serve for comparison of practical magnetic properties of magnets offered by the shop.

Magnetic properties of material grade N35

remanence Br 1,17 - 1,21[T]
coercivity HcB min. 867 [kA/m]
coercivity HcJ min. 955 [kA/m]
energy product (BH)max 263 - 286 [kJ/m3]
Magnetic properties of a particular material, together with its shape, volume, max. working temperature and direction of magnetization have influence on practical magnetic properties of a magnet.
As an example, you will find attached a graph of a course of the II quadrant of magnetic hysteresis loop for a material grade N35.

Physical properties

density ~7,5 [g/cm3]
Vickers’ hardness (HV) ~600 [kg/mm2]
resistivity ~144 [uOhm x cm]

0

0

Magnetic properties of material grade N35: remanence Br 1,17-1,21 [T], coercivity HcB min. 867 [kA/m], coercivity HcJ min. 955 [kA/m], energy product (BH)max 263-286 [kJ/m3] (Magnetic properties of a particular material, together with its shape, volume, max. working temperature and direction of magnetization have influence on practical magnetic properties of a magnet.)

Physical proprieties: density ~7,5 [g/cm3], Vickers’ hardness (HV) ~600 [kG/mm2], resistivity ~144 [uOhm x cm]

Max. working temperature is no more than 80°[C]. (For flat magnets and magnets mounted in the open magnetic circuit working temperature may be insignificantly lower. For high magnets and magnets mounted in the closed magnetic circuit working temperature equals max. working temperature for a given material.) Curie’s temperature is ~ 310°[C]. Temperature coefficient of remanence TK(Br): approx. -0,12 %/°[C]. Temperature coefficient of coercivity TK(HcJ): approx. -0,6 %/°[C].

Direction of magnetization along the height means that one circular surface of a magnet makes the N-pole, while the other – opposite – circular surface refers to the S-pole.

Magnetic flux: ~3560 x 10-3 [mWb], for K(Helmholtz coil constant) = 1,14 × 10-4[m]

Magnetic moment: ~3560 x 10-3 [mWb] × 1,14 × 10-4[m] = ~405,84 x 10-6 [mWb] × [m]

Magnetic field on surface of a magnet with a distance of 0,7 [mm] is ~0,278 [T]

Pull force: ~2,5 [kg]. The pull force was measured by using smooth metal sheet 10 [mm] thick, acting with perpendicular detaching force. The air gap comprised between the metal sheet and a magnet causes reduction in the pull force.

All the numbers quoted were obtained as a result of tests with one specific item in a room temperature and are intended to serve for comparison of practical magnetic properties of magnets offered by the shop.

Anticorrosive protection: coating Ni+Cu+Ni. Do not use in water.

Sintered neodymium magnets are brittle (fragile). A neodymium magnet without housing could break after an impact with another strong magnet.

Weight of the magnet: ~3,10 [g]

We recommend testing of a magnet sample in specific conditions.

As an example, you will find attached a graph of a course of the II quadrant of magnetic hysteresis loop for a material grade N35

N35
MP14X8-4X3N35
4099 Items

Specific References

Download

N35.jpg

Download (77.69k)